Round Shaped Piezoelectric Ceramic For Beauty Vibration Sensor
Piezoelectric ceramic materials are electromechanical transducers: They can convert mechanical energy into electrical energy and vice-versa. Piezoelectric ceramic material from us are used in sensors, actuators, gas ignition and in power transducers for high-power ultrasonic applications.
| Dimension(mm) | Capacity C (pF) |
Weak Field Dissipatio Tgδ (12v) |
Strong Field Dissip ationTg δ (400v) |
Radial Frequency |
Reso nance Impedance |
Thick FrequencyFt (KHz) | Coupling Modulus Kr (%) | Quality Factor Qm | |
| Φ10ｘΦ5ｘ2 | 240±10% | ≤0.5% | ≤1.0% | 153±5% | ≤15 | 1020 | ≥45 | ≥800 | |
| Φ16ｘΦ8ｘ4 | 340±10% | ≤0.5% | ≤1.0% | 95.8±5% | ≤20 | 512 | ≥45 | ≥800 | |
| Φ25ｘΦ10ｘ4 | 935±10% | ≤0.5% | ≤1.0% | 65.5±5% | ≤15 | 512 | ≥45 | ≥800 | |
| Φ30ｘΦ10ｘ5 | 1150±10% | ≤0.5% | ≤1.0% | 58.4±5% | ≤15 | 410 | ≥45 | ≥800 | |
| Φ32ｘΦ15ｘ5 | 1080±10% | ≤0.5% | ≤1.0% | 49.2±5% | ≤15 | 410 | ≥45 | ≥800 | |
| Φ35ｘΦ15ｘ5 | 1430±10% | ≤0.5% | ≤1.0% | 45.5±5% | ≤15 | 410 | ≥45 | ≥800 | |
| Φ38ｘΦ15ｘ5 | 1750±10% | ≤0.5% | ≤1.0% | 43.4±5% | ≤15 | 410 | ≥46 | ≥800 | |
| Φ40ｘΦ15ｘ5 | 1970±10% | ≤0.5% | ≤1.0% | 42.8±5% | ≤15 | 410 | ≥45 | ≥800 | |
| Φ42ｘΦ15ｘ5 | 2200±10% | ≤0.5% | ≤1.0% | 40±5% | ≤15 | 410 | ≥45 | ≥800 | |
| Φ42ｘΦ17ｘ5 | 2110±10% | ≤0.5% | ≤1.0% | 38.8±5% | ≤15 | 410 | ≥45 | ≥800 | |
| Φ45ｘΦ15ｘ5 | 2580±10% | ≤0.5% | ≤1.0% | 38.1±5% | ≤15 | 410 | ≥46 | ≥800 | |
| Φ50ｘΦ17ｘ5 | 3160±10% | ≤0.5% | ≤1.0% | 34.8±5% | ≤15 | 410 | ≥45 | ≥800 | |
| Φ50ｘΦ17ｘ6 | 2430±10% | ≤0.5% | ≤1.0% | 34.8±5% | ≤15 | 315 | ≥45 | ≥800 | |
| Φ50ｘ3 | 5800±10% | ≤0.5% | ≤1.0% | 46±5% | ≤10 | 681 | ≥50 | ≥800 | |
FRQ
1. Reason to the existence of piezoelectricity?
The essential unit which is a rhomboid or cubic shaped cage made up of atoms exists in some atomic lattice structures. Inside the cell, the cage is responsible for holding single semi-mobile ion that has numerous quantum position states. By applying electric field or by distorting the cage (applied strain), the ions post state will consequently shift. The basis or transformation to internal electric field shifts from mechanical strain is provided by coupling between the cage and central ion.
2. How can poling and depoling in piezoceramic materials? Be explained?
The piezoceramics should undergo high electric field for a sometime for the alignment of randomly oriented micro-dipoles in their proper formulation since the chemical composition is not simply responsible for the piezoelectric property of ceramics. This is called “poling” due to alignment resulted from application of high voltage. a “dislodging stress” is exerted on the micro-dipoles due to the application of electric field in the opposite direction if tried. There is only temporary change in polarization if low level field are applied since it bounces back on removal. There is also partly degradation of the polarization along with partial loss of properties when medium fields are applied. Polarization in opposite direction will be resulted if high fields are applied.
Usually the frequency limits of applications are ascertained through the resonances involved with the transducer design and its size and shape. For a piezoceramic sheet, there is no limit for inherent frequency. A sheet of PSI-5A material which is 2.85″ square, .0075″ thick has planar dilatation mode of about 14 KHz and of 13 MHz of thickness mode vibration in the neighborhood. Limiting factors can arise such as the resistive heating of electrodes when considerable current is gathered at large surface area parts during ultrasonic frequencies.
Due to charge leakage the Piezo transducers cannot be used for static force measurements. For transient force measurements they can be applied successfully for only0.1 second.
3.The expected life of piezoelectric material?
There are no tests yet that can determine the “fatigue life”. Our facility has had an operational piezo fan since 1982. Such calculations must involve voltages and mounting.
4.How does temperature effectpiezoceramic transducers?
The pyroelectric properties of piezoceramic are responsible for the appearance of voltage through the any piezo transducer electrodes due to temperature changes. Almost each and every property of piezoceramics is affected by temperature. There exists no general manner regarding it. In accordance to your experiment and calculations, the dependence must be looked upon in that context.
Company introduction:
Established in 1999, Beijing Cheng-cheng Weiye Science and Technology Co., Ltd is a professional manufacturer in ultrasonic transducers, ultrasonic equipment and piezoelectric ceramics.
Notably in 2004, we researched and developed our ultrasonic tubular transducer equipment into a new product that turns the extreme inconvenience brought about by pipeline and vacuum cleaning into an easy task. This product has been widely used in distillation, mix and mill for various chemical procedures and has received much praise from our customers.
Payment:
We accept paypal or T/T, western union etc.
Shipping:
Normally if your quantity is not too much, we ship out by Fedex express economy. Or as your requested by sea or other express, according to your quantity.
Certification: ø
CE, ISO9001, ROSH